Continuous Extrusion PEEK Plate/ Sheet

https://en.chinapeek.com/uploadfiles/107.151.154.88/webid389/source/202101/161136433411.jpg

PEEK Sheets ( Customizable )

L (mm)	W (mm)	H (mm)	G (g)
1000	97	24	3100
1000	116	36	5500
1000	180	167	39200
1000	278	34.5	12600
1000	300	20	7900
1000	385	12	6100
1000	415	15	8200
1000	415	65	35200
1000	800	32.5	34000
1000	240	h	320*h
1000	600	h	790*h
1350	410	h	730*h

PEEK5600G PEEK —5600CF30 PEEK—5600GF30 PEEK—5600LF30

Selection points

To research and develop a satisfied product, primarily, you should select material reasonably. The followings may be your steps:

1.Analyse the applications of material: to learn the using requirements, including product features and application conditions

2.For application, to transfer the property into the property of the material. Designers should take as much trial and simulation experiment of the material as possible.

3.Once confirm the property of the material, designers may search the material of which is suitable for the property. Then condense the scale of material which could be selected, and make sure that there is on material that could be selected missed!

Good facility

Good testing machine

1、Ultrasonic Detector
2、Universal testing machine with high and low temperature
3、 Fusion index instrument
4、Three coordinates measuring instrument

Core advantage

Our Company

Jiangsu junhua plastic always adhere to science and technology, technological progress support scientific and technological innovation. In 2014, We built Changzhou Wujin high-performance specialty engineering plastics engineering and technology research center. We always orient on customer demand, continuously try the implementation of PEEK application and research and development. The company has 16 patents: one slim PEEK sheet continuous extrusion production equipment; a PEEK pipe production technology and a equipment for rotor and preparation methods.

Continuous technological innovation, we get fruitful harvest, the company in 2015 passed the national high-tech enterprise certification, and PEEK products in Jiangsu Province high-tech product certification, and by the US Food and Drug Administration (FDA) food-grade certification, SGS (SGS) quality system certification, the European Union (EU) ROHS testing and other third-party certification.

Below is our PEEK material DATA sheet:

	Condition	Methods	Unit	PEEK5600G	PEEK-5600GF30	PEEK-5600CF30	PEEK-5600LF30
Group				100%PEEK	PEEK+Glass fiber	PEEK+Carbon fiber	PEEK+Carbon fiber+Graphite+PTFE
mechanical properties
Density	23ºC	ISO 1183	g/cm3	1.3	1.51	1.4	1.45
friction coefficient			μ	0.35	0.4	0.28	0.18
Rockwell hardness	23ºC	ASTM D785		99	103	107	102
Shore hardness	23ºC	ISO 868		84.5		87.5	85
Water abs(3.2mm thick)	24h,23ºC	ISO 62-1	%	0.07	0.11	0.04	0.06
Water abs(3.2mm thick)	Balanced water iabsorption,23ºC			0.4		0.3
Tensile strength	Yield,23ºC	ISO 527	Mpa	100
	Crack,23ºC				180	260	140
	Crack,125ºC			50	115	160	95
	Crack,175ºC				60	85	95
	Crack,275ºC			13	35	50	35
Tensile elongation	23ºC	ISO 527	%	45	2.7	1.7	2.2
Tensile modulus	23ºC	ISO 527	Gpa	3.7	11.8	25	12.5
Bending strength	23ºC	ISO 178	Mpa	165	270	380	230
	125ºC			85	190	250
	175ºC			18	80	120
	275ºC			13	50	60
Bending modulus	23ºC	ISO 178	Gpa	4.1	11.3	23	11.5
Compressive strength	23ºC	ISO 604	Mpa	120	250	300	170
	120ºC			70	160	200	110
	200ºC				55	70
	250ºC
Charpy impact strength	Notch,23ºC	ISO 179/1eA	KJ/m2	7	8	7	5
Charpy impact strength	No notch,23ºC	ISO 179/1U		No crack	55	45	35
IZOD impact strength	Notch,23ºC	ISO 180/A	KJ/m2	7.5	10	9.5	6
IZOD impact strength	No notch,23ºC	ISO 180/U		No crack	60	45	35
Thermo properties
Melting point		ISO 3146	ºC	343	343	343	343
Glass transition temperature(Tg)	Initial temperature	ISO 3146	ºC	143	143	143	143
Thermo expansivity	Below Tg along the flow	ISO 11359	ppm/ºC	45	18	5	15
	Below Tg mean value			55	45	40	45
	Above Tg along the flow			120	18	60	20
	Above Tg mean value			140	110	100	115
Distortion temperature	1.8Mpa	ISO 75A-f	ºC	152	328	336	315
Pyroconductivity	23ºC	ASTM C177	W/mºC	0.29	0.3	0.95	0.87
Relative Thermo Index	Electrical	UL 746B	ºC	260	240
	Merchanical(non impact)			240	240		240
	Merchanical(impact)			180	240		180
Mould shrinking percentage	Along the flow	ISO 294-4	%	1	0.3	0.1	0.3
Mould shrinking percentage	vertical to flow	ISO 294-4	%	1.3	0.9	0.5	0.7
Electrical properties
Dielectrical strength	2.5mm Thickness	IEC 60243-1	KV/mm	16	20
CTI	23ºC	IEC 60112	V	150	150
loss tangent	23ºC,1MHz	IEC 60250	n/a	0.003	0.005
Dielectrical constant	23ºC,1kHz	IEC 60250	n/a	2.8	3.2
Volume resistivity	23ºC	IEC 60093	Ωcm	1016	1016	105	1010

JunHua chinaPEEK

Tel: +86-519-86228823

Fax: +86-519-86228826

Website: http://en.chinaPEEK.com

E-mail: chinaPEEK@chinaPEEK.com

Address: Wuyi South Road 377#, Creativity Industry Zone, Wujin District, Changzhou City, Jiangsu Province, China

BACK

Immediately consult